WASSERBRAND
POWERFUL. TENDER. UNTAMED.
CONFIDENT HISTORICAL WATER-STRUCK CONTOURING ON THE FULL BODY.
The light nuanced shades appear lovely but still sharp. The gently rough surfaces and detailed structures are furrowed by water and powerful. It is the skilful blend of untamed and yet delicate accents that gives this simple yet expressive clinker brick slip its striking contemporary look. Because, here, the look of historical water-struck bricks is not manufactured in traditional solid brick, but extruded as a modern clinker brick slip with innovative surface technologies.
Wasserbrand
LAYING HINTS
Window lintel perfectly replicated with angles.
The corner angles are worked using the floating-buttering method.
Use a string to plumb the clinker area. The clinker slips are pressed into the adhesive bed.
The finished surface. Grouting can be done after the appropriate drying time.
With the slurry method, the joints are filled diagonally with the grouting or plaster float. Walls should be worked from top to bottom.
The excess grout is washed off diagonally using a plaster float with a sponge or foam pad.
The finished joint pattern after slurry treatment.
product details
technical specifications, downloads
| Format no. Description | 8140 Clinker brick slips | 8145 Clinker brick slips | 8142 corner | 8147 corner | 8150 Sturzwinkel | 8151 Sturzwinkel |
| Product size (cm) | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| Production size (mm) | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| pieces per bundle | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| pieces per m²/rm incl. joint | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| pieces per pallet | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| m2/lfm pro Paket | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| m2/lfm pro Palette | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| bundles per pallet | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| kg per pallet | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| kg per piece | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| kg pro m2/lfm | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| kg per bundle | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## | ##hidedata## |
| DIN EN 14411 | |
| COLOURS: | 670 sandweiß, 671 kornbeige, 672 zinngrau, 673 naturbeige, 674 lavarot, 675 oxidrot, 676 graumelange, 677 rauchgrau |
| FORMATS: | 8140, 8145 |
| Water absorption (Average value) (EN ISO 10545-3) | ≤ 3 % |
| Scratch hardness of surface (Mohs scale) (minimum individual value) (EN 101) | 6-7 |
| Frost resistance (EN ISO 10545-12) | fulfilled |
| Chemical resistance – except to hydrofluoric acid and its compounds – of tiles (EN ISO 10545-13) | fulfilled |
| Thermal shock resistance (EN ISO 10545-9) | fulfilled |
| Coefficient of thermal expansion from room temperatur (20° C) to 100° C/CE (EN ISO 10545-8) | < 80x10-7K-1 |
| Maximum pore radius (required: rp > 0,2 μm) (DIN 66 133) | 0,59 μm |
| Pore volume (required: Vq > 20 mm3/g (DIN 66 133) | 32,1 mm3/g |