&bsp;
WASSERBRAND
POWERFUL. TENDER. UNTAMED.
CONFIDENT HISTORICAL WATER-STRUCK CONTOURING ON THE FULL BODY.
The light nuanced shades appear lovely but still sharp. The gently rough surfaces and detailed structures are furrowed by water and powerful. It is the skilful blend of untamed and yet delicate accents that gives this simple yet expressive clinker brick slip its striking contemporary look. Because, here, the look of historical water-struck bricks is not manufactured in traditional solid brick, but extruded as a modern clinker brick slip with innovative surface technologies.
Wasserbrand
LAYING HINTS
Window lintel perfectly replicated with angles.
The corner angles are worked using the floating-buttering method.
Use a string to plumb the clinker area. The clinker slips are pressed into the adhesive bed.
The finished surface. Grouting can be done after the appropriate drying time.
With the slurry method, the joints are filled diagonally with the grouting or plaster float. Walls should be worked from top to bottom.
The excess grout is washed off diagonally using a plaster float with a sponge or foam pad.
The finished joint pattern after slurry treatment.
product details
technical specifications, downloads
| Description | Clinker brick slips | corner | Läuferwinkel | Clinker brick slips | corner | Läuferwinkel | Clinker brick slips | corner | Läuferwinkel | |
| Nominal size | DF | DF | DF | NF | NF | NF | bar shape | - | - | |
| Production size (mm) | 240 x 52 x 12 | 240 x 115 x 52 x 12 | 240 x 115 x 52 x 12 | 240 x 71 x 12 | 240 x 115 x 71 x 12 | 240 x 115 x 71 x 12 | 490 x 40 x 12 | 240 x 115 x 40 x 12 | 240 x 115 x 40 x 12 | |
| pieces per bundle | 52 | 14 | 6 | 39 | 14 | 4 | 40 | 24 | 6 | |
| pieces per m2/rm incl. joint | 64,00 | 16,13 | 4,00 | 48,00 | 12,50 | 4,00 | 38,31 | 19,23 | 4,00 | |
| pieces per pallet | 4212 | 910 | 684 | 3159 | 910 | 456 | 1440 | 1560 | 684 | |
| m2/rm per bundle | 0,81 | 0,87 | 1,50 | 0,81 | 1,12 | 1,00 | 1,04 | 1,25 | 1,50 | |
| m2/rm per pallet | 65,81 | 56,42 | 171,00 | 65,81 | 72,80 | 114,00 | 37,59 | 81,12 | 171,00 | |
| bundles per pallet | 81 | 65 | 114 | 81 | 65 | 114 | 36 | 65 | 114 | |
| kg per pallet | 1314,00 | 420,00 | 614,00 | 1349,00 | 562,00 | 488,00 | 691,00 | 521,00 | 573,00 | |
| kg per piece | 0,31 | 0,46 | 0,90 | 0,43 | 0,62 | 1,07 | 0,48 | 0,33 | 0,84 | |
| kg per m2/rm | 19,97 | 7,45 | 3,59 | 20,50 | 7,73 | 4,28 | 18,39 | 6,42 | 3,35 | |
| kg per bundle | 16,22 | 6,49 | 5,39 | 16,65 | 8,65 | 4,28 | 19,20 | 8,02 | 5,03 |
| DIN EN 14411 | |
| COLOURS: | 4409 sandweiß, 4413 kornbeige, 4415 naturbeige, 4472 zinngrau, 4475 graumelange, 4477 racuhgrau, 4425 lavarot, 4427 oxidrot |
| FORMATS: | DF, NF, Riegel |
| Water absorption (Average value) (EN ISO 10545-3) | ≤ 3 % |
| Scratch hardness of surface (Mohs scale) (minimum individual value) (EN 101) | 6-7 |
| Frost resistance (EN ISO 10545-12) | fulfilled |
| Chemical resistance – except to hydrofluoric acid and its compounds – of tiles (EN ISO 10545-13) | fulfilled |
| Thermal shock resistance (EN ISO 10545-9) | fulfilled |
| Coefficient of thermal expansion from room temperatur (20° C) to 100° C/CE (EN ISO 10545-8) | < 80x10-7K-1 |
| Maximum pore radius (required: rp > 0,2 μm) (DIN 66 133) | 0,59 μm |
| Pore volume (required: Vq > 20 mm3/g (DIN 66 133) | 32,1 mm3/g |